RO 5200 Tantalum Enhancement Ring for Medical Industry 0.5 - 0.7mm Diameter

RO5200  tantalum Enhancement ring for  Medical industry

Quick Details:

Chemical Composition:tantalum

Type:Heating Tube

outside diameter:0.5mm-0.7mm 

wall thickness :0.02

melting point:3017 °C

boiling point:5458 °C

crystalline phases:α ,β

grade: RO5200.RO5252,RO5255

Tensile strength  :207 MPa min.
Yield strength      :138 MPa min.
               

Chemical composition:  

                O                   0.0150   %max 
                C                   0.0100   %max 
                N                   0.0100   %max 
                H                   0.0015   %max 
                Fe                  0.0100   %max 
                Ti                   0.0100   %max 
                Ni                   0.0100   %max 
                Si                   0.0050   %max 
                Mo                 0.0200   %max 
                W                  0.0500   %max 
                Nb                 0.1000   %max 
                Ta                 Remainder

 Appllication:Medical industry,invasiveness of surgical procedures 

Feature:

 is dark (blue-gray),dense, ductile, very hard, easily fabricated, and highly conductive of heat and electricity. The metal is 

renowned for its resistance to corrosion by acids; in fact, at temperatures below 150 °C tantalum is almost 

completely immune to attack by the normally aggressive aqua regia. It can be dissolved with hydrofluoric acid 

or acidic solutions containing the fluoride ion and sulfur trioxide, as well as with a solution of potassium 

hydroxide. Tantalum's high melting poin
RO 5200 Tantalum Enhancement Ring for Medical Industry 0.5 - 0.7mm Diameter